依托材料合成与制备技术积累的综合研发实力,为不同领域客户研发领先市场的功能材料产品。
可镀制增透膜、高反膜、偏振膜、分光膜、透明导电膜等,主要应用于光通讯、激光、液晶显示、幕墙玻璃等领域需要的各种光学镜头、滤光片、红外膜及功能薄膜。
*此表为氧化物的汇总
Formula |
Typical Purity |
Refractive Index(n) at 550nm |
Transmission Range(nm) |
Melting Point(℃) |
Evaporation Temperature (℃) at 10-4Torr |
Density (g/cm3) |
Z-ratio |
Product Form |
Al2O3 |
99.99% |
1.64 |
200~5000 |
2045 |
~2100 |
3.97 |
0.336 |
Granules, Melted |
CeO2 |
99.99% |
2.35 |
400~16000 |
2600 |
~1600 |
7.13 |
N.A. |
Granules, Tablets |
Cr2O3 |
99.9% |
2.24-i0.07 |
600-8000 |
2435 |
1900-2000 |
5.21 |
0.4 |
Granules |
Cr+SiO |
99.95% |
N.A. |
N.A. |
N.A. |
N.A. |
N.A. |
N.A. |
Granules Tablets |
Fe2O3 |
99.9% |
2.72-i0.11 |
400~12000 |
1565 |
1600-1800 |
5.24 |
N.A. |
Granules Tablets |
HfO2 |
99.99% |
1.9~2.07 |
220~12000 |
2812 |
2300~2700 |
9.68 |
1.0 |
Granules Tablets |
ITO |
99.99% |
2.0 |
400~8000 |
N.A. |
~1400 |
N.A. |
N.A. |
Granules Tablets |
LaAlO3 |
99.99% |
1.7 |
220~10000 |
2080 |
~2100 |
N.A. |
N.A. |
Granules |
LaTiO3 |
99.99% |
2.0 |
360~7000 |
1800 |
2200~2300 |
5.9 |
1.0 |
Granules |
MgO |
99.9% |
1.7 |
230~9000 |
2800 |
~2600 |
3.58 |
0.411 |
Granules, Crystal |
Nb2O5 |
99.99% |
2.2 |
320~8000 |
1530 |
~1600 |
4.47 |
1.0 |
Granules Tablets |
SiO2 |
99.99% |
1.45~1.47 |
190~2000 |
1650±50 |
1800~2200 |
2.648 |
1.000 |
Granules |
SiO |
99.9% 99.99% |
1.9~2.1 |
550~8000 |
1702 |
1200~1600 |
2.13 |
0.870 |
Granules Tablets |
TiO |
99.9% |
2.4 |
400~12000 |
1750 |
1800~2000 |
4.90 |
N.A. |
Granules Tablets |
TiO2 |
99.99% |
2.2~2.5 |
400~12000 |
1640 |
2000~2200 |
4.26 |
0.400 |
Granules Tablets |
Ti3O5 |
99.9% |
2.35 |
400~10000 |
1760 |
1900~2100 |
4.47 |
0.4 |
Granules Melted |
Ta2O5 |
99.99% |
2.07~2.13 |
300~10000 |
1880 |
2000~2200 |
8.2 |
0.3 |
Granules Tablets Target |
TiO2+Ta2O5 |
99.99% |
2.25~2.3 |
400~8000 |
N.A. |
2300~2500 |
N.A. |
N.A. |
Granules Tablets |
TiO2+Nb2O5 |
99.99% |
2.2~2.3 |
400~8000 |
N.A. |
2300~2500 |
N.A. |
N.A. |
Granules Tablets |
Y2O3 |
99.99% |
1.75 |
250~8000 |
2680 |
~2400 |
5.01 |
1.0 |
Granules Tablets |
Yb2O3 |
99.99% |
1.93 |
280~8000 |
2372 |
~1900 |
9.17 |
N.A. |
Granules Tablets |
ZrO2 |
99.99% |
2.05 |
250~8000 |
N.A. |
~2200 |
N.A. |
N.A. |
Granules |
ZrO2+TiO2 |
99.99% |
2.1 |
400~8000 |
N.A. |
2200-2400 |
N.A. |
N.A. |
Granules Tablets |
ZrO2+Al2O3 |
99.99% |
1.7~1.9 |
250~8000 |
N.A. |
2400-2550 |
N.A. |
N.A. |
Granules Tablets |
ZrO2+Y2O3 |
99.99% |
1.9 |
250~8000 |
N.A. |
2500-2600 |
5.55 |
N.A. |
Granules Tablets |